O fasi Polyamide 6—e masani ona ta'ua o fasi Nylon 6—ua faaigoaina ona o sootaga amide (–CO–NH–) o lo'o i totonu o latou macromolecules. E masani ona foliga mai o ni granules pa'epa'e ma lapotopoto, o fasi Nylon 6 e iai le melting point e 210–220°C ma le vevela e tusa ma le 300°C pe a pala. E mafai ona solo i le phenol ma le sulfuric acid vevela, e iai fo'i ona uiga lelei i le insulation eletise, ma e tete'e lelei i alkalis ma le ele. O le Nylon o le alava sili ona tete'e i le olo o alava fa'apitoa uma.
Tau: E mafai ona feutana'i USD/MT
Taulaga: Qingdao MOQ: 1Mt Numera o le Kamupani: 25038-54-4 Tulafono HS: 3908101101 Totogi: TT, LC
Miloina o ie mo lavalava, alava ma filo tau alamanuia, ata tifaga Co-Extrusion.
Afifiina
Taga Tele 800Kg, 28MT/40HQ
Meatotino
Metotia o Su'ega
Tuutuuga o Su'ega
Iunite
I'uga o le Su'ega
Vasega
LX 275 BRT
Malōlōga Fa'atatau
FZ/T 51004-2011
25℃, 96%H2SO4, m:v = 1:100
/
2.75±0.03
Kalapu faapitoa
/
/
g/cm³
1.12
Malosiaga o le fua
ASTM D638
50mm/min
Mpa
67.00
Fa'alavelave i le taimi e motusia ai
ASTM D638
50mm/min
%
239.57
Modulus o le tensile
ASTM D638
1mm/min
Mpa
2405.52
Malosiaga fa'apipi'i
ASTM D790
2mm/min
Mpa
100.62
Modulus o le fetu'una'i
ASTM D790
2mm/min
Mpa
3317.33
Malosiaga o le a'afiaga ua fa'ailogaina e Izod
ASTM D256
23℃
J/m
48.98
Saosaoa o le tafe o le tele o le liusuavai
ASTM D1238
235℃, 2.16kg
g/10min
17.89
Vevela o le fa'asesēina i lalo o le avega
ASTM D648
1.82MPa, 3.2mm
℃
44.10
Teena o Fa'amatalaga:
O fuainumera o loʻo i luga o tau masani ia mo le faʻasologa o oloa talafeagai, o loʻo avea ma faʻasinomaga mo oloa filifilia e le tagata faʻatau, ma o tau moni e noatia i le COA o le oloa.