| Leai. | Meatotino Resin | Tau masani | Iunite | Metotia o Su'ega |
| 1 | Kalave Fa'apitoa, 23℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Fa'aitiitia o le Popole, 23℃, 3.2mm, 23℃ | 0.4-0.7 | % | ASTM D955 |
| 3 | Fua Fa'atatau o le Tafe o le Liusuavai, 220℃, 10kg | 22 | g/10min | ASTM D1238 |
| 4 | Malosiaga o le Tete'e i le Gaosiga, 23 ℃, 50mm/min, 3.2mm | 49 | MPa | ASTM D638 |
| 5 | Fa'aumiumi o le Tete'e i le Gaosiga, 23 ℃, 50mm/min, 3.2mm | 5 | %, (Maualalo) | ASTM D638 |
| 6 | Fa'aloaloa o le Tete'e i le Tape, 23'℃, 50mm/min, 3.2mm | 10 | %, (Maualalo) | ASTM D638 |
| 7 | Fa'asologa o le Malosiaga, 23℃, 50mm/min, 3.2mm | 2350 | MPa | ASTM D638 |
| 8 | Malosiaga Fa'alava, 23℃, 15mm/min, 3.2mm | 78 | MPa | ASTM D790 |
| 9 | Modulus Fa'alava, 23℃, 15mm/min, 3.2mm | 2550 | MPa | ASTM D790 |
| 10 | Malosiaga o le Izod, Fa'ailoga, 3.2mm, 23℃ | 220 | J/m | ASTM D256 |
| 11 | Malosiaga o le Izod, Fa'ailoga, 3.2mm, -30℃ | 90 | J/m | ASTM D256 |
| 12 | Malosiaga o le Izod, Fa'ailoga, 6.4mm, 23℃ | 220 | J/m | ASTM D256 |
| 13 | Malosiaga o le Izod, Fa'ailoga, 6.4mm,-30℃ | 90 | J/m | ASTM D256 |
| 14 | Ma'a'a o Rockwell, Fua-R | 110 | / | ASTM D785 |
| 15 | HDT, Edgewise, 1.82MPa, 6.4mm, E le'i fa'apipi'iina | 85 | °C | ASTM D648 |
| 16 | VICAT, 50N, 50℃/h | 92 | °C | ASTM D1525 |
| 17 | RTI Eletise | 95 | °C | UL 746B |
| 18 | RTI Mechanical ma le A'afiaga | 95 | °C | UL 746B |
| 19 | RTI Mechanical e aunoa ma se A'afiaga | 95 | °C | UL 746B |
| 20 | Mugofie, 1.5mm | HB | / | UL 94 |
| 21 | Mugofie, 3.0mm | HB | / | UL 94 |